SABIC® PPcompound 8600
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 886Hfq_SABIC-PPcompound-8600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8600 is a mineral filled modified polypropylene. This material combines high flow with a high impact, high stiffness level and a very low shrinkage and CLTE. This material has a very broad processing window with a reasonable esthical performance. Typical applications include automotive exterior parts such as large thin wall zero gap bumper designs and vertical body panels. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 8600 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.45 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 19.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 17.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | > 400 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | No Break | ||
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 3.5E-5 | cm/cm/°C | |
| 23 to 80°C | 4.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8045 | Colorite Polymers | PVC, Unspecified | Unichem |
| Evatane® 28-05 | Arkema | EVA | Evatane® |
| Kuraray Poval® PVA 225 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| Plaslube® HDPE TL10 | Techmer Engineered Solutions | HDPE | Plaslube® |
| Sylvin 8036-65 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |