RELENE® 52GB001
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | seYgnw_RELENE-52GB001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 52GB001 is a High Molecular Weight High Density Polyethylene (HMHDPE) blow moulding grade with very good impact strength, stiffness and good ESCR produced. It possesses medium molecular weight distribution and easy processability. 52GB001 can readily be processed on most of the large volume blow moulding machines with accumulators. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/10.0 kg | 0.40 | g/10 min | |
| 190°C/21.6 kg | 2.3 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Compression Molded) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Compression Molded) | 10 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V945 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP ESD 683 | RTP Company | ABS | RTP |
| ExxonMobil™ LLDPE LL 1002YB Cast | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Haprez™ 3748 | Hapco Inc. | TP, Unspecified | Haprez™ |
| Daelim Po1y® XP5400 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |