Sup-tech B101EX
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sdhLUG_Sup-tech-B101EX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech B101EX is a Polyamide 6 (Nylon 6) product. It can be processed by extrusion or injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | DIN 53479 |
| Melt Mass-Flow Rate (MFR) | 1.0 to 2.0 | g/10 min | DIN 53735 |
| Molding Shrinkage | 0.010 to 0.014 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 1.8 | % | |
| Saturation, 23°C | 8.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 70.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 70 | % | DIN 53452 |
| Flexural Modulus | 1980 | MPa | DIN 53457 |
| Flexural Stress | 105 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 62.0 | °C | |
| Melting Temperature | 220 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 265 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP8615 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TOTAL Polyethylene Lumicene® M 1835 | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| 3M™ Dyneon™ Fluoroelastomer FT 2350 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| OnFlex™ U 5370A-E0077 | PolyOne Corporation | TPE | OnFlex™ |
| Sumiliteresin® PR-53473 | SBHPP | Phenolic | Sumiliteresin® |