CERTENE™ HI-2553
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YnlfyR_CERTENE-HI-2553.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HI-2553 is a certified prime copolymer designed for molding thin wall applications requiring good resistance to low temperature and good balance of mechanical properties. HI-2553 features high flow, fast cycling, easy processability, good impact strength, high gloss surfaces, good dimensional stability and warpage resistance. HI-2553 applications include multicavity margarine and yogurt tubs, ice cream pails, frozen food containers, deep drawn housewares, and over-caps. HI-2553 recommended processing temperature is 210 to 230°C. with mold @ 20 to 40°C. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, Compression Molded, F50) | 1.00 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 150 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Compression Molded) | 1140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 31.5 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Brittleness Temperature | -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 230 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 280.8 | RTP Company | Nylon 66 | RTP |
| Reon 67GER01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| Zhongfa PC G2820 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC | Zhongfa |
| IDI STC 4450B | IDI Composites International | TS, Unspecified | IDI STC |
| IROGRAN® A 95 E 4813 | Huntsman Corporation | TPU-Polyester | IROGRAN® |