TEKAMID™ TA210K40
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sKiGFV_TEKAMID-TA210K40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TA210K40 is a mineral filler 40% reinforced polyamide 66. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 90.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3 | 7350 | MPa | ASTM D790 |
| Flexural Strength 4 | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 245 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 | °C | ASTM D648 |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Injection Speed: 30 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MegaCarb® PC-FR510 | Mega Polymers | PC | MegaCarb® |
| Zytel® RS 30G30HSL BK038A | DuPont Performance Polymers | Nylon 610 | Zytel® RS |
| Estane® 58219 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| PETILEN S 23/59 | PETKIM Petrokimya Holding A.S. | PVC, Rigid | PETILEN |
| Sylvin 86030-82 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |