DENKA STYROL MW-1-321
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA STYROL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sHQpTL_DENKA-STYROL-MW-1-321.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The high tensile strength of DENKA STYROL MW is achieved through our proprietary macromolecular technologies. It is a well-balanced polystyrene resin, with a high tensile strength as well as good moldability. Overturning the traditional understanding that PS resin is "hard and brittle", this product's applications have been expanded to include large packaging cases (and the like), advancing the world of PS resin and becoming a synonym for ultra-strong PS. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 75 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 47.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | < 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3300 | MPa | ISO 178 |
| Flexural Stress 2 | 102 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 74.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 90.0 | % | ISO 13468 |
| Haze (2000 µm) | 0.30 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RALUPOL® UP 2200 | RASCHIG GmbH | Polyester, TS | RALUPOL® |
| Niuk 50RNG30 | Shanghai Niuk New Plastic Technology Co., Ltd. | Nylon 66 | Niuk |
| Adiprene® LFP 2950A | Chemtura | PUR-Capro/PPDI | Adiprene® |
| Hostacom G3 R11 105290 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Lumiplas® LD7750 | LG Chem Ltd. | PC | Lumiplas® |