Sarlink® TPV X5735B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sH3pe4_Sarlink-TPV-X5735B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink® TPV X5735B is a Thermoplastic Vulcanizate (TPV) material. It is available in Asia Pacific, Europe, Latin America, or North America. Typical application of Sarlink® TPV X5735B: Automotive |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.928 | g/cm³ | ASTM D792 |
| -- | 0.930 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, 5 sec, Extruded | 34 | ||
| Shore A, 5 sec, Injection Molded | 36 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 0.800 | MPa | |
| Flow : 100% Strain | 1.70 | MPa | |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Across Flow : Break | 3.30 | MPa | |
| Flow : Break | 2.60 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 530 | % | |
| Flow : Break | 210 | % | |
| Tear Strength - Across Flow | |||
| -- | 9.98 | kN/m | ASTM D624 |
| -- 1 | 10 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 12 | % | |
| 70°C, 22 hr | 23 | % | |
| 125°C, 70 hr | 42 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -5.0 | % | ASTM D573, ISO 188 |
| 100% Strain, 135°C, 1000 hr | 4.0 | % | ASTM D573 |
| 150°C, 168 hr | 2.0 | % | ASTM D573, ISO 188 |
| 100% Strain, 150°C, 168 hr | 8.0 | % | ASTM D573 |
| 100% Strain 135°C, 1000 hr | 4.0 | % | ISO 188 |
| 100% Strain 150°C, 168 hr | 8.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | 15 | % | |
| 150°C, 168 hr | 12 | % | |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Shore A, 135°C, 1000 hr | 0.0 | ||
| Shore A, 150°C, 168 hr | 1.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 110 | % | ASTM D471, ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary @ 206/s | |||
| 200°C | 210 | Pa·s | ISO 11443 |
| 200°C | 210 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIGITRON 10020 GF | Ovation Polymers Inc. | PC | RIGITRON |
| RTP 199 X 137777 C | RTP Company | PP, Unspecified | RTP |
| Monprene® CP-39040D XRD (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Sylvin 6168-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Ferro PP MPP40FA05NA | Ferro Corporation | PP, Unspecified | Ferro PP |