DOWLEX™ SC 2106G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mpGEVK_DOWLEX-SC-2106G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ SC 2106G is processable at high line speeds. Films made from DOWLEX SC 2106G Polyethylene Resin exhibit excellent stretchability, tear and impact resistance, as well as exceptional optical properties. Applications:
Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 23 µm | 6.20 | MPa | ASTM D882 |
| TD : Yield, 23 µm | 5.50 | MPa | ASTM D882 |
| MD : Break, 23 µm | 38.0 | MPa | ASTM D882 |
| TD : Break, 23 µm | 21.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 23 µm | 500 | % | ASTM D882 |
| TD : Break, 23 µm | 780 | % | ASTM D882 |
| Dart Drop Impact 3(23 µm) | 140 | g | ASTM D1709A |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 23 µm | 320 | g | ASTM D1922 |
| TD : 23 µm | 530 | g | ASTM D1922 |
| Film tensile properties-maximum stretch to penetration 5 | 155 | Internal method | |
| Film Tensile Properties-Maximum Elongation 6 | 260 | % | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 7(45°, 23.0 µm) | 93 | ASTM D2457 | |
| Haze 8(23.0 µm) | 0.60 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 熔体温度：220-280°C 冷却辊温度：20-60°C 脱离速度：150-450 米/分 建议的厚度范围：10-60 µm |
| Note Message | |
|---|---|
| 1 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 2 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 3 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 4 . | Method B; Cast film, 250 m/min; Cooling roller 25 c. |
| 5 . | Cast film, 250 m/min, cooling roller 25°C; Measured on test bench; Maximum prestretching before penetration of sharp probe. |
| 6 . | Cast film, 250 m/min, cooling roller 25°C; Measured on the test bench. |
| 7 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 8 . | Cast film, 250 m/min; Cooling roller 25 c. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-152D A/B | Shin-Etsu Silicones of America | Silicone Rubber, RTV-2 | Shin-Etsu RTV |
| Nipol® Polyblend DN517SCR | Zeon Corporation | PVC+NBR | Nipol® Polyblend |
| Advanced Composites ATX639MX2N | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Jiangsu Sinarise JM9513 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| OmniCarb鈩?PC GR10 | OMNI Plastics, LLC | PC | OmniCarb™ |