LNP™ STAT-KON™ REP349 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sGwrHT_LNP-STAT-KON-REP349-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON REP349 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone, 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Wear Resistant. Also known as: LNP* STAT-KON* Compound RCL-4534 FR Product reorder name: REP349 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.67 | % | ISO 294-4 |
| Flow : 24 hr | 0.18 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19300 | MPa | ASTM D638 |
| -- | 18200 | MPa | ISO 527-2/1 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 168 | MPa | |
| Break | 168 | MPa | |
| Tensile Elongation | |||
| Yield | 1.8 | % | ASTM D638, ISO 527-2 |
| Break | 1.8 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 15200 | MPa | ASTM D790 |
| -- | 15300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 255 | MPa | ASTM D790 |
| -- | 263 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 3 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.60 | J | ASTM D3763 |
| -- | 2.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 250 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 251 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 233 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 234 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 to 1.0E+9 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN A-352 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| RTP 899 X 88188 | RTP Company | Acetal (POM) Homopolymer | RTP |
| Minlon® 73M40 NC010 | DuPont Performance Polymers | Nylon 6 | Minlon® |
| Vinylbond 95-950-50 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Cellophane™ K140HB20/23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |