TAROLOX 10 G4 X0
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sAvxR7_TAROLOX-10-G4-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT glass fibre reinforced 20%, self extinguishing UL94 V0 also at low thickness, good flow, good surface finish, good mechanical properties, high dimensional stability. UL94 V0 approved all colours at 0,97 mm. UL746B approved. IMQ T180 approved for lampholders. Available: all colors, release agent (W), without PBDE/PBDF. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 to 1.59 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.60 | % | |
| Across Flow | 0.60 to 0.90 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.050 | % | ASTM D570, ISO 62 |
| Saturation | 0.25 | % | ASTM D570 |
| Saturation, 23°C | 0.25 | % | ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 165 | MPa | ISO 178 |
| Break | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 5.5 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ISO 1817, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 215 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 75.0 | °C | UL 746B |
| -- 2 | 90.0 | °C | IEC 60216 |
| -- 3 | 130 | °C | IEC 60216 |
| -- 4 | 130 | °C | IEC 60216 |
| -- 5 | 160 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ASTM D1525, ISO 306/A50 8 6 |
| -- | 210 | °C | ASTM D1525, ISO 306/B50 9 7 |
| Ball Pressure Test (205°C) | Pass | VDE 0470 | |
| Melting Temperature | 220 to 225 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 250 | V | |
| Solution B | 175 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 31 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 20000 hrs |
| 3 . | Short Term |
| 4 . | Heat Stabilized, 20000 hrs |
| 5 . | Heat Stabilized, Short Term |
| 6 . | Rate A (50°C/h), Loading 1 (10 N) |
| 7 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 4010 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| AFFINITY™ GA 1000R | The Dow Chemical Company | TPO (POE) | AFFINITY™ |
| AKROMID® A3 K1 FR black 950089 (2246) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Huafon HF-1275AP | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| ISOTHANE® 1055D | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |