POLYFORT® FPP 3722
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2LkGLH_POLYFORT-FPP-3722.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP, 35% Calcium Carbonate, Low Emission |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 25.0 | MPa | ASTM D638 |
| Flexural Modulus 3 | 2800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 100 | °C | |
| 1.8 MPa, Unannealed | 57.0 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 35 | % | ASTM D5630 |
| Note Message | |
|---|---|
| 1 . | 5x7 in plaque |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 211 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TECHNYL® A R 218 V25 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| MTEGRITY™ HDPE HD700 | M. Holland Company | HDPE Copolymer | MTEGRITY™ HDPE |
| WELLAMID Nylon 6600 GS 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Cri-Line LC-815-LV | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |