Generic PP Random Copolymer
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rizQeA_Generic-PP-Random-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Random Copolymer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 - 0.902 | g/cm³ | ASTM D792 |
| 23°C | 0.891 - 0.910 | g/cm³ | ISO 1183 |
| -- | 0.900 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.52 - 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.25 - 38 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.20 - 28 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 2.40 - 67.1 | cm³/10min | ISO 1133 |
| Spiral Flow | 50.0 - 80.0 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 1.3 - 1.8 | % | ASTM D955 |
| 23°C | 1.5 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 79 - 100 | ASTM D785 | |
| 23°C | 75 - 98 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 52 - 80 | ASTM D2240 | |
| 23°C | 58 - 68 | ISO 868 | |
| Ball Indentation Hardness | 44.8 - 60.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 892 - 1200 | MPa | ASTM D638 |
| 23°C | 790 - 1300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 24.4 - 30.5 | MPa | ASTM D638 |
| Yield, 23°C | 19.6 - 31.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 19.3 - 44.3 | MPa | ASTM D638 |
| Fracture, 23°C | 14.5 - 40.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 6.0 - 28 | % | ASTM D638 |
| Yield, 23°C | 10 - 16 | % | ISO 527-2 |
| Fracture, 23°C | 78 - 510 | % | ASTM D638 |
| Fracture, 23°C | 46 - 510 | % | ISO 527-2 |
| Apparent Bending Modulus (23°C) | 740 - 830 | MPa | ASTM D747 |
| Flexural Modulus | |||
| 23°C | 766 - 1270 | MPa | ASTM D790 |
| 23°C | 573 - 1260 | MPa | ISO 178 |
| Flexural Stress (23°C) | 6.50 - 25.0 | MPa | ISO 178 |
| Coefficient of Friction | 0.15 - 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 - 80 | µm | |
| secant modulus | |||
| MD | 345 - 790 | MPa | ASTM D882 |
| 23°C | 190 - 801 | MPa | ISO 527-3 |
| Tensile Strength | |||
| MD : Yield | 18.0 - 22.6 | MPa | ASTM D882 |
| MD : Fracture | 20.3 - 40.5 | MPa | ASTM D882 |
| Fracture, 23°C | 29.0 - 39.6 | MPa | ISO 527-3 |
| 23°C | 25.0 - 42.5 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Fracture | 490 - 760 | % | ASTM D882 |
| Fracture, 23°C | 500 - 760 | % | ISO 527-3 |
| Instrumented Dart Impact (23°C) | 1.00 - 30.3 | J | ISO 7765-2 |
| Seal Initiation Temperature | 105 - 115 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 22 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 5.0 - 200 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 26 - 82 | J/m | ASTM D256 |
| 23°C | 3.4 - 9.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 39 - 72 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 23.4 - 36.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 72.8 - 100 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 54.5 - 85.7 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 49.1 - 55.3 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 45.6 - 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 125 - 140 | °C | ASTM D1525 |
| -- | 65.4 - 137 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 128 - 150 | °C | |
| -- | 132 - 150 | °C | DSC |
| -- | 140 - 150 | °C | ISO 11357-3 |
| -- | 125 - 150 | °C | ASTM D3418 |
| -- | 125 - 148 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 79 - 132 | ASTM D2457 | |
| Haze | 0.40 - 17 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 220 | °C | |
| Middle Temperature | 205 - 221 | °C | |
| Front Temperature | 205 - 227 | °C | |
| Processing (Melt) Temp | 206 - 250 | °C | |
| Mold Temperature | 27.5 - 40.4 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Random CopolymerThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 185 - 206 | °C | |
| Cylinder Zone 2 Temp. | 185 - 206 | °C | |
| Cylinder Zone 3 Temp. | 185 - 206 | °C | |
| Cylinder Zone 4 Temp. | 185 - 206 | °C | |
| Cylinder Zone 5 Temp. | 185 - 206 | °C | |
| Melt Temperature | 194 - 301 | °C | |
| Die Temperature | 199 - 216 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Random CopolymerThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 91 C 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| Altuglas® BS 520 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Karina CRYSTAL PVC COMPOUND 72/204-D-AT-H | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1/CF/20/TF/15/SI/2 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Sylvin 8790-95 Red 6229 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |