MAJORIS DFR918
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ri0O8f_MAJORIS-DFR918.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR918 is a halogen free flame retardant compound UL 94 VO, intended for injection moulding. The product is available in natural but other colours can be provided on request DFR918 is especially designed for technical parts. In addition to have good flame retardant properties, this product has an extremely low level of toxicity in case of fire. DFR918 is mainly intended for the injection moulding of electrical components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.6 - 1.8 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 27.0 | MPa | ISO 527-2 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 124 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SG722 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| QR Resin QR-3000-GF30 | QTR, Inc. | PET | QR Resin |
| TECHNYL STAR™ AFX 218 V60 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL STAR™ |
| Adell Polyamide AF-10-669 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| ULTEM™ 9085 resin | SABIC Innovative Plastics | PEI | ULTEM™ |