ASTAPET™ PC/PET MDA267
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAPET™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rKBXcD_ASTAPET-PC-PET-MDA267.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAPET™ MDA267 is an alloy of Polycarbonate and 100% recycled polyethylene terephthalate (PET). Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: Astapet™ MDA267-U ]. ASTAPET™ MDA267 is a development grade, the typical values detailed on this data sheet are based on limited data and are subject to frequent review |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (285°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1(3.00 mm) | 0.40 - 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(3.20 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 200 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2200 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 76.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 900 | J/m | ASTM D256 |
| Dart Drop Impact (3.20 mm) | 70.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 116 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 77.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 83.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ASTM D1525 6 |
| -- | 114 | °C | ASTM D1525 7 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| CLTE, ASTM D696: 6e-5 to 7e-5 cm/cm/°CElongation at Break, ASTM D638, 3.2 mm, 5.0 mm/min: >200%Glow Wire Temperature, AS 2420, 1.6 mm: 550°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 245 - 255 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 255 - 265 | °C | |
| Processing (Melt) Temp | 260 - 270 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C | |
| Injection Pressure | 60.0 - 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 6.0 | kN/cm² |
| Injection instructions |
|---|
| Nozzle Temperature: Do not exceed stock temperature |
| Note Message | |
|---|---|
| 1 . | D2 type |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 压 力1 (10N) |
| 7 . | 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu E500 | Cheng Yu Plastic Company Limited | PC+PET | Cheng Yu |
| Desmoderm® KB2W | Covestro - PUR | PUR-Ester | Desmoderm® |
| Fainplast PVC GS 75/O | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Polyrocks 168S | Polyrocks Chemical Co., Ltd | PP, Unspecified | Polyrocks |
| AvaSpire® AV-651 GF50 | Solvay Specialty Polymers | PAEK | AvaSpire® |