TROGAMID® T T5004
| Category: | Nylon 6/3T , Polyamide 6/3T Copolymer |
| Manufacturer: | Evonik Industries AG |
| Trademark: | TROGAMID® T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qe4uwU_TROGAMID-T-T5004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TROGAMID® T and BX consist of terephthalic acid and 2,2,4- /2,4,4-trimethyl hexamethylene diamine, a chemical composition that is responsible for their amorphous structure. This makes TROGAMID® T transparent in contrast to the semi-crystalline high-performance plastics of High Performance Polymers. The amorphous structure also results in low molding shrinkage and low tendency to warp. In addition to the basic products, a range of specially equipped compounds is also available. The product line fits a wide range of applications and satisfies many requirement profiles. TROGAMID® T5004 Permanently transparent polyamide with UV stabilizer and improved outdoor weathering behavior for injection molding, extrusion, and blow molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.12 | g/cm³ | ISO 1183 |
| Viscosity Number | 125 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 86 | ISO 868 | |
| Ball Indentation Hardness | 150 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 90.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2500 | MPa | |
| 1000 hr | 1300 | MPa | |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 6.0 | kJ/m² | |
| 0°C, Complete Break | 9.0 | kJ/m² | |
| 23°C, Complete Break | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 0°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 150 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A |
| -- | 150 | °C | ISO 306/B |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 5.5E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 5.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 50 Hz | 4.20 | ||
| 23°C, 1 MHz | 3.30 | ||
| 23°C, 100 MHz | 4.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 50 Hz | 0.017 | ||
| 23°C, 1 MHz | 0.028 | ||
| 23°C, 100 MHz | 0.024 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- 2 | 575 | V | |
| Solution A | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| Glow Wire Flammability Index (1.00 mm) | 800 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 875 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| 2 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin RP 3301 Natural | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| Moplen 2152HOXP | LyondellBasell Industries | PP Homopolymer | Moplen |
| Wellamid® GF30-60 XE-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| AKROMID® B3 GFM 10/20 1 grey (4561) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| CP PRYME® Nylon 6 N213HSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |