MAJORIS CT203 - 5761
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gi3Qi7_MAJORIS-CT203---5761.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CT203 - 5761 is a white, 20% mineral filled grade intended for injection moulding. The product is available in natural (CT203) and black (CT203 - 8229)but other colours can be supplied on request. CT203 - 5761 has been developed especially for the car industry, to be used in interior parts and also for the white good industry especially for applications requiring high detergent resistance and heat stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 4.0 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.7 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.3 | kJ/m² | ISO 179/1eA |
| 23°C | 2.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 19 | kJ/m² | ISO 179/1eU |
| 23°C | 52 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A |
| -- | 105 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Fogging | DIN 75201 | ||
| 100°C/16h | 5.0E-4 | g | DIN 75201 |
| 100°C/3h | 95 | % | DIN 75201 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SN501G50AH | RJM International, Inc. | Nylon 6 | RJM |
| Starex BF-0677HF | SAMSUNG SDI CO., LTD. | MABS | Starex |
| Sumitomo Silicone SI 9550 | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| Sylvin 9423-55 NATURAL | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| Luran® S Q440 | Styrolution | ASA | Luran® S |