Order Products : sales@su-jiao.com
VAMPORAN 3028 V1
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPORAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qYVLgR_VAMPORAN-3028-V1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V1, halogen free, 30% glass fiber reinforced, good dimensional stability, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.22 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 10 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 105 | °C | ASTM D648A |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 1 |
| RTI Elec | 100 | °C | UL 746 |
| RTI Imp | 100 | °C | UL 746 |
| RTI Str | 100 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | ||
| 3.20 mm | V-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2865 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| WanBlend® WHT-890E5 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| Elvaloy® 742 | DuPont Packaging & Industrial Polymers | EVA | Elvaloy® |
| Infino XF-4150 | SAMSUNG SDI CO., LTD. | PPA | Infino |
| Panlite® MN-3600HA | TEIJIN LIMITED | PC | Panlite® |