| Ultramid T KR 4355 G7 BK00564 is a 35% glass fiber reinforced injection molding PA6/6T grade featuring high toughness, stiffness, and strength, low water absorption, and high melting point (295 C). After the material has been conditioned, its mechanical properties remain stable up to 60 C. This grade is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Break, -40°C | 279 | 270 | MPa | |
| Break, 23°C | 210 | 200 | MPa | |
| Tensile Strain (Break, 23°C) | 3.0 | 3.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 17 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 100 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 270 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 295 | -- | °C | ISO 3146 |
| CLTE | ||||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 5.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 4.20 | 4.40 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.030 | IEC 60250 | |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® G3301HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| apilon 52® TL 65 | API SpA | TPU-Polyether | apilon 52® |
| LNP™ LUBRICOMP™ QFL36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |
| LUVOCOM® 1105-0699-F | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| EnviroTPE 80A | West Michigan Compounding | TPE | EnviroTPE |