Desmopan® DP 3660DU
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YHOyqh_Desmopan-DP-3660DU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; transparent up to 6 mm wall thickness; hydrolysis-stabilised; with special UV stabilizers; with release agent; good wear resistance; Application; Sports shoe soles; Hoses, non-reinforced; Profiles |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1230 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 98 | ||
| Shore D, 15 sec | 60 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 53.7 | MPa | |
| 10% Strain, 23°C | 12.1 | MPa | |
| 50% Strain, 23°C | 22.1 | MPa | |
| 100% Strain, 23°C | 28.1 | MPa | |
| 300% Strain, 23°C | 37.8 | MPa | |
| Tensile Strain 4(Break, 23°C) | 320 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 23.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 2.61 | GPa | |
| 20°C | 0.444 | GPa | |
| 60°C | 0.129 | GPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 31 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5(23°C) | 170 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 24 | % | |
| 70°C, 24 hr | 47 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 215 to 235 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Melt Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 N L | RTP Company | PESU | RTP |
| TPC PVC SG66Z | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Colorite 66 Series 6566 | Colorite Polymers | PVC, Unspecified | Colorite 66 Series |
| Ferro PP LPP26BC63UL-BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Haysite Plastics ETS | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |