VALOX™ 8032U resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q9acet_VALOX-8032U-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX 8032U is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. Applications: appliance housings, door handles, mirror brackets. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.53 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.40 to 0.80 | % | |
| Flow : 3.20 mm | 0.40 to 0.80 | % | |
| Across Flow 2 | 0.60 to 1.0 | % | |
| Across Flow : 3.20 mm | 0.60 to 1.0 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.16 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 9950 | MPa | ASTM D638 |
| -- | 9500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 115 | MPa | ASTM D638 |
| Yield | 145 | MPa | ISO 527-2/5 |
| Break 5 | 115 | MPa | ASTM D638 |
| Break | 145 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 2.0 | % | ASTM D638 |
| Yield | 2.4 | % | ISO 527-2/5 |
| Break 7 | 2.0 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 8450 | MPa | ASTM D790 |
| -- 9 | 8500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 210 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 165 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 30.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 12 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 48 | J/m | ASTM D256 |
| 23°C | 57 | J/m | ASTM D256 |
| -30°C 13 | 8.0 | kJ/m² | ISO 180/1A |
| 0°C 14 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 15 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 470 | J/m | ASTM D4812 |
| 23°C | 480 | J/m | ASTM D4812 |
| -30°C 16 | 40 | kJ/m² | ISO 180/1U |
| 23°C 17 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 8.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 208 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 18 | 217 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 190 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 19 | 195 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ASTM D1525, ISO 306/A50 11 20 |
| -- | 202 | °C | ASTM D1525, ISO 306/B50 12 21 |
| -- | 204 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 60°C | 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 27 | kV/mm | |
| 1.60 mm, in Oil | 23 | kV/mm | |
| 3.20 mm, in Oil | 15 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 8.0E-4 | ||
| 60 Hz | 8.0E-4 | ||
| 1 MHz | 0.013 | ||
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 255 to 280 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 265 to 275 | °C | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 60.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 120*10*4 mm |
| 19 . | 120*10*4 mm |
| 20 . | Rate A (50°C/h), Loading 2 (50 N) |
| 21 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1203-30 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| RTP ESD C 260H | RTP Company | Nylon 66 | RTP |
| ACCUTECH™ HPA338G30M5C002L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Delta PCR-1G40 | Delta Polymers | PC | Delta |
| Gallonprene® GP210-5502L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |