TECHNYL STAR® AFX 216 V60 GREY 2327 Datasheet,Nylon 66,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL STAR® AFX 216 V60 Grey 2327 is a high flow polyamide 66 resin, reinforced with 60% of glass fibre, for injection moulding. Due to its outstanding flow caracteristics, this grade shows exceptional processing behaviour and excellent surface aspect of the finished part.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 60% filler by weight
Features	Good dimensional stability Excellent appearance Rigidity, high High liquidity
Uses	Gear Large household appliances and small household appliances
Agency Ratings	UL QMFZ2
Appearance	Grey
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)
Resin ID (ISO 1043)	PA66-GF60

Physical	Dry	Conditioned	Unit	Test Method
Density	1.69	--	g/cm³	ISO 1183/A
Water Absorption (23°C, 24 hr)	0.52	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
23°C	19600	--	MPa	ASTM D638
23°C	22000	16500	MPa	ISO 527-2/1A
Tensile Strength
Fracture, 23°C	250	--	MPa	ASTM D638
Fracture, 23°C	260	195	MPa	ISO 527-2/1A
Tensile Elongation
Yield, 23°C	2.0	--	%	ASTM D638
Fracture, 23°C	2.0	--	%	ASTM D638
Fracture, 23°C	2.2	2.9	%	ISO 527-2
Flexural Modulus
23°C	18000	--	MPa	ASTM D790
23°C	18000	13200	MPa	ISO 178
Flexural Strength
23°C	370	--	MPa	ASTM D790
23°C	400	300	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	15	15	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	90	87	kJ/m²	ISO 179/1eU
Notched Izod Impact (23°C)	170	--	J/m	ASTM D256

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
1.8 MPa, not annealed	253	--	°C	ASTM D648
1.8 MPa, not annealed	245	--	°C	ISO 75-2/Af
Melting Temperature	262	--	°C	ISO 11357-3

Flammability	Dry	Conditioned	Test Method
Flame Rating			UL 94
0.8 mm	HB	--	UL 94
1.6 mm	HB	--	UL 94
3.2 mm	HB	--	UL 94

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	265 - 275	°C
Middle Temperature	270 - 280	°C
Front Temperature	280 - 290	°C
Mold Temperature	60 - 90	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL STAR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yhbYFn_TECHNYLSTARAFX216V60GREY2327.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Resirene READ 9600 5V RAF	Resirene, S.A. de C.V.	PS (HIPS)	Resirene
RTP 1005 TFE 20	RTP Company	PBT	RTP
Tekuform C9	TEKUMA Kunststoff GmbH	Acetal (POM) Copolymer	Tekuform
Sup-tech P9000	Shanghai Suptech Engineering Plastics Co. Ltd.	PP, Unspecified	Sup-tech
NORYL™ WCV063 resin	SABIC Innovative Plastics	PPE+SEBS+Polyolefin	NORYL™