Kingfa MF-40
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q7EMOq_Kingfa-MF-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa MF-40 is a polypropylene material, which contains 40% mica filler. This product is available in North America or Asia Pacific,. The main features of Kingfa MF-40 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 73.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 11 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 7080 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 104 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 56 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm, Injection Molded) | 150 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Filler Content, ISO3451/1, Method A: 40% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumiflex® K K58DL13 | Mitsubishi Chemical Corporation | PVC Elastomer | Sumiflex® K |
| Moplen HA748L | PolyMirae | PP, High Crystal | Moplen |
| Geon™ Vinyl Flexible 90463 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| HiFill® PA6 GF40 RM HS BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Latene® 11 MDT05-01 | LATI S.p.A. | PP Homopolymer | Latene® |