Ultramid® B3G8
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pzekWo_Ultramid-B3G8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A glass fibre reinforced injection moulding grade suitable for auto pedals and modules. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.80 | -- | % | ISO 294-4 |
| Flow direction | 0.24 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.4 - 6.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.6 - 2.0 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 13000 | 8200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 205 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | 4.6 | % | ISO 527-2 |
| Tensile Creep Modulus 1(1000 hr) | 3300 | -- | MPa | ISO 899-1 |
| Flexural Modulus | 10500 | 7400 | MPa | ISO 178 |
| Flexural Stress | 290 | 205 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | ISO 179/1eA |
| 23°C | 14 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 90 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/A | |||
| -30°C | 12 | -- | kJ/m² | ISO 180/A |
| 23°C | 16 | 12 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 1.0E-5 - 1.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 5.5E-5 - 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1400 | -- | J/kg/°C | |
| Thermal Conductivity | 0.36 | -- | W/m/K | DIN 52612 |
| Maximum operating temperature- short cycle operation | 200 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Pass | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+10 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 4.00 | 6.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | 0.13 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time: <10 min. |
| Note Message | |
|---|---|
| 1 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA6 A1LG6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| Buna® EP T 9650 | LANXESS Corporation | EPDM | Buna® EP |
| apilon 52® 8011 | API SpA | TPU-Polyester | apilon 52® |
| FHR Polypropylene 13T25A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Dapol® D2102F | Fudow Co., Ltd. | DAP | Dapol® |