Bayblend® FR3010 IF
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pgLP7w_Bayblend-FR3010-IF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; increased heat resistance; Vicat/B 120 temperature = 108 °C; improved flammability; UL recognition 94 5VB (1.5 mm); glow wire test (GWFI): 960 °C (2.0 mm); improved flow compared to FR3010. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/5.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 25 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 88.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ISO 306/B50 |
| -- | 108 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.6E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 5VB | ||
| 3.00 mm | 5VA |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 210 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOLIT® P 1300 K | VESTOLIT GmbH & Co. KG | PVC, Unspecified | VESTOLIT® |
| Formolene® L62009B | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| P-FLEX H 200 | Putsch Kunststoffe GmbH | ABS | P-FLEX |
| Honghai CPE 130A | Weifang Honghai Plastics Technology Co., Ltd. | CPE | Honghai |
| Sylvin 8784-77 Black 280 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |