Latistat 48/9900-03
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latistat |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pOE3zT_Latistat-48-9900-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Dissipative product based on EVA. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.3 to 1.6 | % | |
| Flow : 2.00 mm | 1.3 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 10.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C | 250 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 45.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 35.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 50.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+2 | ohms | ASTM D257 |
| Volume Resistivity | 4.0E+2 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V80B | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| SABIC® PP 680K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| ELASTOSIL® LR 3003/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Generic TPO | Generic | TPO | Generic |
| Iupilon® MB4405U | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |