POLYform C M20
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYform C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pSZ2Qv_POLYform-C-M20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYform C M20 is an Acetal (POM) Copolymer product. It is available in Asia Pacific or Europe. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 to 2.0 | % | |
| Flow | 1.8 to 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2 |
| Tensile Stress | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 14 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 163 | °C | ISO 306/A50 |
| -- | 150 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M2101R (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| Ultramid® A3WG10 | BASF Corporation | Nylon 66 | Ultramid® |
| Akulon® Ultraflow K220-HGM44 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| HAIPLEN H30 G4 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Karina NATURAL PVC COMPOUND -E TR-75701-25/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |