Exxtral™ Performance Polyolefin CNK010
| Category: | TPO , Polypropylene, Compounded (TPO) |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Exxtral™ Performance Polyolefin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nu3mtY_Exxtral-Performance-Polyolefin-CNK010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The invention relates to a special thermoplastic polyolefin resin with low melting property and excellent low-temperature impact strength, and is used in injection molding or extrusion molding automobile occasions. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Flexural Stress | 31.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C, complete fracture | 3.0 | kJ/m² | ISO 179 |
| 0°C, complete fracture | 4.0 | kJ/m² | ISO 179 |
| 23°C, local fracture | 25 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C, Partial Break) | 27 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 76.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.0 | °C | ISO 75-2/A |
| Legal statement |
|---|
| 本产品不宜在与食品接触的应用中使用。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1865A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Karina CLEAR PVC COMPOUND -E 65/200-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kepital® F20-03M | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| SEQUEL® 1492-UV NH647 MET GD | LyondellBasell Industries | PP, Unspecified | SEQUEL® |
| PENTAMID AB S GV30 H black | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |