DOW™ LDPE 501I
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pMhq2n_DOW-LDPE-501I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 4.22 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 221 | J/cm³ | ASTM D882 |
| TD : 51 µm | 183 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 12.2 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.8 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 25.5 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 19.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 650 | % | ASTM D882 |
| TD : Fracture, 51 µm | 730 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 88 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 440 | g | ASTM D1922 |
| TD : 51 µm | 480 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.2 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 111 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 76 | ASTM D2457 | |
| Haze (50.8 µm) | 6.7 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 217 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm) 30:1 L/D 螺杆类型：单跨双混合 模具间隙：40 密尔 (1.02 mm) 熔体温度：422°F (217°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：90 rpm 冷冻线高度：30 分钟 (762 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| mPact™ D139 | Chevron Phillips Chemical Company LLC | mLLDPE | mPact™ |
| Ecobarrier® 0712ML | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |
| KumhoSunny PC/ABS HAC6010FG | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Karina BLACK PVC COMPOUND 834-48/ 1-A-ERM-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hylex® P1307L3 HB | Entec Polymers | PC | Hylex® |