RTP 3003
| Category: | PMP , Polymethylpentene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aboNsu_RTP-3003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 160 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 266 to 304 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon TG1930H | RheTech, Inc. | Nylon 6 | Rhelon |
| Akulon® M-1016 | DSM Engineering Plastics | Nylon 66 | Akulon® |
| ELASTOSIL® LR 3015/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| GAPEX® RPP40EB81HB BLACK | Ferro Corporation | PP Homopolymer | GAPEX® |
| MAJORIS DW100 - 8229 | AD majoris | PP Homopolymer | MAJORIS |