LUVOCOM® 1105-1330 Datasheet,PEEK,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1105-1330 is a polyetheretherketone (PEEK) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1105-1330 are: flame retardant/rated flame Flame Retardant chemical resistance Wear-resistant Lubrication Typical application areas include: engineering/industrial accessories textile/fiber Aerospace Automotive Industry medical/health care

General Information
Additive	PTFE lubricant
Features	Low friction coefficient Good chemical resistance Good wear resistance Lubrication Hydrolysis stability Self-lubricating Flame retardancy
Uses	Pump parts Bushing Gear Textile applications Engineering accessories Aerospace applications Application in Automobile Field Medical/nursing supplies Bearing
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.36	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (380°C/10.0 kg)	20.0	cm³/10min	ISO 1133
Molding Shrinkage	1.0 - 1.6	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3500	MPa	ISO 527-2
Tensile Stress (Break)	85.0	MPa	ISO 527-2
Tensile Strain (Yield)	6.0	%	ISO 527-2
Flexural Modulus	3000	MPa	ISO 178
Flexural Stress	115	MPa	ISO 178
Flexural Strain at Flexural Strength	8.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	260	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	70	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	250	°C	UL 746B

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	150	°C
Hot air dryer, B	120	°C
Drying Time
Hot air dryer, A	3.0 - 6.0	hr
Hot air dryer, B	6.0 - 8.0	hr
Suggested Max Moisture	0.050	%
Rear Temperature	360 - 370	°C
Middle Temperature	380 - 390	°C
Front Temperature	390 - 400	°C
Nozzle Temperature	360 - 380	°C
Processing (Melt) Temp	390	°C
Mold Temperature	170 - 190	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	PEEK , Polyetheretherketone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pG36k2_LUVOCOM-1105-1330.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sinvicomp SIF4569	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
Daicel PP PNAS3	Daicel Polymer Ltd.	PP, Unspecified	Daicel PP
LNP™ THERMOCOMP™ Lexan_LGK3020 compound	SABIC Innovative Plastics	PC	LNP™ THERMOCOMP™
SABIC® SUPEER™ 8115L	Saudi Basic Industries Corporation (SABIC)	mLLDPE	SABIC® SUPEER™
ESTOPLAST ZK 8508WW93	Ester Industries Ltd.	PC+ABS	ESTOPLAST ZK