Moplen HP2981
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pFhm8r_Moplen-HP2981.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP2981 is a polypropylene homopolymer developed for the production of transparent cast film. It is formulated with slip agent. Films made with Moplen HP2981 show very high transparency, a high gloss and a good printability after corona treatment. Main applications are the production of shopping bags and packaging of snacks, pasta, bakery products, books, blankets, hosiery and shirts. For regulatory information please refer to Moplen HP2981 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1250 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | 570 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic | 0.25 | ||
| Static | 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD | 800 | MPa | ASTM D882 |
| Tensile Strength - MD | ASTM D882 | ||
| Yield | 21.0 | MPa | |
| Break | 32.0 | MPa | |
| Tensile Elongation - MD | ASTM D882 | ||
| Yield | 5.0 | % | |
| Break | 610 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 153 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 100 µm) | 88 | ASTM D2457 | |
| Haze (100 µm) | 1.5 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV 30 Natural | Radici Plastics | Nylon 66 | Radilon® |
| Niuk 23ND40 | Shanghai Niuk New Plastic Technology Co., Ltd. | PC+ABS | Niuk |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Cheng Yu A779 | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| HAIPLEN EP50 T7 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |