CABELEC® CA3178
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p0t1Dt_CABELEC-CA3178.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® 3178 is an electrically conductive compound based on conductive carbon black, dispersed in nylon 6. It has been formulated for injection moulding applications. It has been developed to give a balanced property profile with permanent electrical conductivity. CABELEC® 3178 has been specially designed for packaging and electronic product handling applications where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosives, electronic components and pigments. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.20 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2(275°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow 3 | 1.5 to 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 4(Shore D, 15 sec) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5 | ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 45.0 | MPa | |
| Tensile Strain 6(Break) | 15 | % | ISO 527-2 |
| Flexural Modulus 7 | 2700 | MPa | ISO 178 |
| Flexural Stress 8 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Notched Izod Impact Strength 9(23°C) | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 10(1.8 MPa, Unannealed) | 66.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 11 | 215 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 12 | 1.0E+3 | ohms | Internal Method |
| Volume Resistivity 13 | 1.0E+2 | ohms·cm | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Rear Temperature | 220 to 275 | °C | |
| Middle Temperature | 220 to 275 | °C | |
| Front Temperature | 220 to 275 | °C | |
| Nozzle Temperature | 220 to 275 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E047 |
| 4 . | CTM E023 |
| 5 . | CTM E041 |
| 6 . | CTM E041 |
| 7 . | CTM E040A |
| 8 . | CTM E040B |
| 9 . | CTM E044A |
| 10 . | CTM E038 |
| 11 . | CTM E039 |
| 12 . | CTM E042E |
| 13 . | CTM E043B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T20P252-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| MIRASON™ 11P | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| Boda FF2870 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Elastoflex® W 5666/103 | BASF Polyurethanes GmbH | PUR-MDI | Elastoflex® |
| Sylvin 9077-75 LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |