Fluoroplex MB 555 - GML
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | UNIFLON |
| Trademark: | Fluoroplex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MdgVvk_Fluoroplex-MB-555---GML.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fluoroplex MB 555-GML is a polytetrafluoroethylene (PTFE) product, which contains 55% bronze filler. It can be processed by sintering or injection molding and is available in North America or Latin America. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.75 - 3.85 | g/cm³ | Internal method |
| Contractility- Sintering | 0.90 - 1.9 | % | Internal method |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Sintering Temperature - Maximum | 360 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 - 74 | Internal method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 16.0 | MPa | Internal method |
| Tensile Elongation (Break) | 80 | % | Internal method |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Code: 010003901 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 21.0 - 25.0 | °C | |
| Injection Pressure | 49.0 - 58.8 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QAMAR HB18N | SPDC Ltd. | LLDPE | QAMAR |
| TOTAL Polystyrene 814 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| UNISOFT TPE™ ST-20A-NT-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| ECOGRAN® PEHDE Soufflage BLK | Eurocompound Polymers | HDPE | ECOGRAN® |
| Elastron® G P.G401.A50.N | Elastron USA, Inc. | SEBS | Elastron® G |