VYTEEN ABS 2904 DX9
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Lavergne Group |
| Trademark: | VYTEEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oyB5c9_VYTEEN-ABS-2904-DX9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vyteen ABS 2904 DX9 is a Daimler Chrysler DX9 black, recycled ABS high impact high flow with balanced impact / stiffness properties designed for injection molding applications. Features
Typical Applications
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 37.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2100 | MPa | ASTM D790 |
| Flexural Strength 3 | 62.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Dart Drop Impact | ASTM D5420 | ||
| -29°C | 4.00 | J | ASTM D5420 |
| 23°C | 15.0 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 45 | mm/min | SAE J369 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.30 | % | |
| Rear Temperature | 185 - 195 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Nozzle Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 220 - 235 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Injection Pressure: MediumBack Pressure: Medium |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 MG GB 20 | RTP Company | Nylon 66 | RTP |
| CALP 4700G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| DIAMALOY ABSPC 750 HF | Network Polymers, Inc. | PC+ABS | DIAMALOY ABSPC |
| Lucon® PX6103F | LG Chem Ltd. | PBT | Lucon® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |