LNP™ THERMOTUF™ V1000UXC compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Z080B_LNP-THERMOTUF-V1000UXC-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF V1000UXC is a compound based on unfilled Super Tough Nylon resin. Added feature of this material is: UV Stabilized. Also known as: LNP* THERMOTUF* Compound V-1000 UV HP Product reorder name: V1000UXC |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 | g/cm³ | ASTM D792 |
| -- | 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 2.1 to 2.3 | % | ASTM D955 |
| Across Flow : 24 hr | 2.5 to 2.7 | % | ASTM D955 |
| Across Flow : 24 hr | 2.6 | % | ISO 294-4 |
| Flow : 24 hr | 2.2 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.60 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1710 | MPa | ASTM D638 |
| -- | 1650 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/5 |
| Break 3 | 39.0 | MPa | ASTM D638 |
| Break | 41.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 57 | % | ASTM D638 |
| Yield | 150 | % | ISO 527-2/5 |
| Break 5 | 85 | % | ASTM D638 |
| Break | 170 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 1700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 55.2 | MPa | ASTM D790 |
| -- | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 49.8 | J | ASTM D3763 |
| -- | 49.4 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 192 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 6 | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 193 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 147 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.3E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 48.9 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 10 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 80*10*4 mm |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Colorite Rigid PVC 2502 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Colorite CS Series CS8036CS | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Huaxia Shenzhou PFA DS708-B | Shandong Huaxia Shenzhou New Material Co., Ltd. | PFA | Huaxia Shenzhou |
| KEBATER® PBT BF115 | BARLOG plastics GmbH | PBT | KEBATER® |
| LNP™ LUBRICOMP™ DL004 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |