LNP™ LUBRICOMP™ Lexan_WR5210R compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | owGNg5_LNPLUBRICOMPLexanWR5210Rcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Wear resistant, 7% PTFE filled PC. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 53.8 | MPa | ASTM D638 |
| Fracture | 55.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 75 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2030 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 180 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 38.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 127 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 52 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PA66 MC66G25FR | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |
| ADEKA EP-4520S | Adeka Corporation | Epoxy | ADEKA |
| Aristech Acrysteel® IMA | Aristech Acrylics LLC | Acrylic, Unspecified | Aristech |
| Karina MBPEB WHITE -E 1000/0085-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SABIC® LDPE PCG81 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |