Generic PC+Polyester
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oCSKf2_Generic-PC-Polyester.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC+Polyester This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 - 1.20 | g/cm³ | ASTM D792 |
| 23°C | 1.17 - 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 3.0 - 30 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 3.80 - 27.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.50 - 0.76 | % | ASTM D955 |
| Transverse flow : 23°C | 0.50 - 0.66 | % | ASTM D955 |
| 23°C | 0.59 - 0.86 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.12 - 0.51 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 - 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1160 - 2480 | MPa | ASTM D638 |
| 23°C | 1470 - 2690 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 42.4 - 62.0 | MPa | ASTM D638 |
| Yield, 23°C | 54.3 - 62.3 | MPa | ISO 527-2 |
| Fracture, 23°C | 43.5 - 66.0 | MPa | ASTM D638 |
| Fracture, 23°C | 44.4 - 62.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 4.9 - 6.1 | % | ASTM D638 |
| Yield, 23°C | 5.0 - 6.0 | % | ISO 527-2 |
| Fracture, 23°C | 97 - 150 | % | ASTM D638 |
| Fracture, 23°C | 99 - 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1160 - 2350 | MPa | ASTM D790 |
| 23°C | 1570 - 2330 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 75.4 - 93.7 | MPa | ASTM D790 |
| 23°C | 58.0 - 92.2 | MPa | ISO 178 |
| Yield, 23°C | 64.9 - 98.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 - 73 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 70 - 1100 | J/m | ASTM D256 |
| 23°C | 7.0 - 11 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 76.7 - 95.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 79.0 - 124 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 123 - 138 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.0 - 114 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 77.6 - 112 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 90.0 - 132 | °C | ASTM D1525 |
| -- | 91.0 - 133 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 7.0E-5 - 1.2E-4 | cm/cm/°C | ASTM E831 |
| Flow | 5.9E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.9E-5 - 1.1E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 6.7E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.23 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+11 - 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.5E+11 - 2.4E+15 | ohms·cm | ASTM D257 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 85.0 - 89.0 | % | ASTM D1003 |
| Haze | 1.0 - 2.2 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 120 | °C | |
| Drying Time | 4.0 - 5.1 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 60 | % | |
| Rear Temperature | 243 - 261 | °C | |
| Middle Temperature | 248 - 271 | °C | |
| Front Temperature | 254 - 281 | °C | |
| Nozzle Temperature | 240 - 281 | °C | |
| Processing (Melt) Temp | 254 - 269 | °C | |
| Mold Temperature | 51.0 - 77.0 | °C | |
| Back Pressure | 0.300 - 0.668 | MPa | |
| Screw Speed | 60 - 75 | rpm | |
| Vent Depth | 0.017 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC+PolyesterThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 6850-70A | Vi-Chem Corporation | TPE | Sevrene® |
| Sylvin 8476-90UV Red 6257 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ZELAS® MC715R4 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | ZELAS® |
| Grivory® GVL-5H black 9839 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Moplen EP310D | LyondellBasell Industries | PP Impact Copolymer | Moplen |