VESTAKEEP® 2000 CF30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAKEEP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o97dSM_VESTAKEEP-2000-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Carbon fiber-reinforced (30%) polyether ether ketone VESTAKEEP 2000 CF30 is a medium-viscosity, carbon fiber-reinforced (30%) polyether ether ketone for injection molding. The semi-crystalline polymer features superior mechanical, thermal, and chemical resistance. Parts made from VESTAKEEP 2000 CF30 are self-extinguishing. VESTAKEEP 2000 CF30 can be processed by common injection molding machines for thermoplastics. We recommend a melt temperature between 380°C and 400°C during the injection molding process. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (380°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 180°C, 2.00 mm | 0.40 | % | |
| Flow : 180°C, 2.00 mm | 0.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 240 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 8.0 | kJ/m² | |
| 23°C, Complete Break | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Complete Break | 45 | kJ/m² | |
| 23°C, Complete Break | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 340 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 330 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 343 | °C | ISO 306/A |
| -- | 340 | °C | ISO 306/B |
| Melting Temperature 2 | 340 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+6 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 380 to 400 | °C | |
| Mold Temperature | 160 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | determined on 2 mm sheets with film gate at rim mold temperature 180°C |
| 2 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer S80H | Precision Polymer Engineering Ltd. | Silicone | Precision Polymer |
| Mecoline I RDX 1230 F | Melos GmbH | TP, Unspecified | Mecoline |
| Durez® 33553 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Geon™ Vinyl Rigid Extrusion 87775 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Durethan® BKV 25 FN27 000000 | LANXESS GmbH | Nylon 6 | Durethan® |