Nylux 6/G20FL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | Nylux |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o6dKUd_Nylux6G20FL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylux 6/G20FL is a polyamide 6 (nylon 6) product, which contains a 33% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.30 - 0.70 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | MPa | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 195 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 235 - 275 | °C | |
| Mold Temperature | 70 - 120 | °C | |
| Back Pressure | 0.300 - 0.500 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermx® TE4004 | Celanese Corporation | PCT | Thermx® |
| TRIBOCOMP® PA612 CF30 TS0 | EPIC Polymers | Nylon 612 | TRIBOCOMP® |
| AKROMID® A3 GF 60 black (2432) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Fainplast PVC CKL 76/V | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LIHAN® B705 | Nanjing Lihan Chemical Co., Ltd. | Nylon 6 | LIHAN® |