LNP™ THERMOCOMP™ UX04509 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o3qWfp_LNP-THERMOCOMP-UX04509-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UX04509 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound PDX-U-04509 Product reorder name: UX04509 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.38 | g/cm³ | |
| -- | 1.36 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.50 | % | |
| Across Flow : 24 hr | 0.50 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.29 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 36800 | MPa | ASTM D638 |
| -- | 34400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 307 | MPa | ASTM D638 |
| Yield | 293 | MPa | ISO 527-2/5 |
| Break 3 | 307 | MPa | ASTM D638 |
| Break | 293 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.3 | % | ASTM D638 |
| Yield | 1.1 | % | ISO 527-2/5 |
| Break 5 | 1.3 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 29300 | MPa | ASTM D790 |
| -- 7 | 28800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 425 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 424 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 424 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| 23°C 10 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 11 | 47 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.20 | J | ASTM D3763 |
| -- | 2.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 303 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 301 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 289 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 283 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF 9203 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Fainplast PVC GS 70 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| INSTRUC PA66GF20IM | Infinity LTL Engineered Compounds | Nylon 66 | INSTRUC |
| Pearlthane® 11T85E | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| PIVINEL™ SEM-P3 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |