LNP™ LUBRICOMP™ DFL36P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nwtyFk_LNP-LUBRICOMP-DFL36P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features of this material include: Exceptional Processing. Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4036 EP Product reorder name: DFL36P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.11 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9770 | MPa | ASTM D638 |
| -- | 9520 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 113 | MPa | ASTM D638 |
| Break | 112 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 2.2 | % | ASTM D638 |
| Break 4 | 2.8 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 8920 | MPa | ASTM D790 |
| -- 6 | 8840 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 172 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 176 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.48 | ||
| vs. Itself - Static | 0.62 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 14.6 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 96.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 8 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D4812 |
| 23°C 9 | 42 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 17.3 | J | ASTM D3763 |
| -- | 5.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 133 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 133 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86011-85FUV Clear Black 288 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TPC PVC SF580 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Ferro PP TPP20AJ46BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Epoxies, Ect. 60-7156 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Petrotene® PP A3 C40 NTLA010 PH309 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |