LNP™ STAT-KON™ OE004AE compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nmIh0z_LNP-STAT-KON-OE004AE-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* OE004AE is a compound based on PPS - Branched resin containing 20% Carbon Fiber. Added features of this material are: Easy Molding, Electrically Conductive. Also known as: LNP* STAT-KON* Compound OC-1004 EM Product reorder name: OE004AE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 27200 | MPa | ASTM D638 |
| -- | 19100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 163 | MPa | ASTM D638 |
| Yield | 146 | MPa | ISO 527-2/5 |
| Break 3 | 163 | MPa | ASTM D638 |
| Break | 146 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 0.86 | % | ASTM D638 |
| Yield | 0.81 | % | ISO 527-2/5 |
| Break 5 | 0.86 | % | ASTM D638 |
| Break | 0.80 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 15700 | MPa | ASTM D790 |
| -- 7 | 16100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 208 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 215 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 47 | J/m | ASTM D256 |
| 23°C 9 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 250 | J/m | ASTM D4812 |
| 23°C 10 | 13 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 279 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 263 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 262 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 GI-1000 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Texin® 285 | Covestro - PUR | TPU-Polyester | Texin® |
| Vital-Line SHE5240B | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Pearlthane® D91F65D | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® |
| POLYCOMPO PP J702LB | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |