Braskem EVA CN8092
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ngygdT_Braskem-EVA-CN8092.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CN8092 is an Ethylene-Vinyl Acetate copolymer (EVA) which has a molecular structure that provides easy processability, adhesion, resilience, low hardness and good moisture and gas barrier properties. It is a non-halogen resin with excellent thermal stability, low oligomers content and low influence on organoleptic properties of the products. The rheological properties of this resin allow processability in extrusion equipments for cast and tubular films. Additives: Antioxidant Application:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 15.5 | wt% | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, Molded | 91 | ASTM D2240 | |
| Shore D, Molded | 44 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (Compression Molded) | 72.0 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 4.70 | MPa | ASTM D638 |
| Fracture, molding | 17.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 720 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.0 | °C | ASTM D1525 1 |
| Peak Melting Temperature | 90.0 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 225 | °C |
| Extrusion instructions |
|---|
| Blow Film Extrusion: Melt Temperature: 135 to 150°C Blow Up Ratio: BUR - 2 to 3.1 Die Gap: .8 to 1.0 mm Cast Film Extrusion: Melt Temperature: 205 to 210°C Chill Roll Temperature: 25°C |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPR 40G BK701 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| MAXAMID™ PA666G33-NC010 | Pier One Polymers, Inc. | Nylon 66/6 | MAXAMID™ |
| Geon™ Vinyl Rigid Extrusion 87416 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Edgetek™ AT-30GF/000 BK004 | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Hyundai EP PA66 LD610 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |