Hiprolon® 11 ESNWHL P20
| Category: | Nylon 1012 , Polyamide 1012 |
| Manufacturer: | Arkema |
| Trademark: | Hiprolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nLf80P_Hiprolon-11-ESNWHL-P20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hiprolon® 11 ESNWHL P20 is a polyamide produced from a renewable source. This black grade is plasticized and designed for extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 440 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 47.0 | °C | ISO 75-2/A |
| Melting Temperature | 187 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA 1012-P, EHL, 22-004 | ISO 1874 | |
| Renewable Carbon Conent | > 41 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 210 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 TFE 10 SI 2 | RTP Company | PP Homopolymer | RTP |
| SPESIN® KP212G30V0GRS | Kolon Plastics, Inc. | PBT | SPESIN® |
| DINAPLEN® PPH1S07 G20V0-4137 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Fainplast PVC RKS 01183/W-OM | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| ESENTTIA 07R87 | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |