Halar® 1400LC
| Category: | ECTFE , Ethylene Chlorotrifluoroethylene Copolymer |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Halar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nLZQ8f_Halar-1400LC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Halar® 1400LC is an Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion. Important attributes of Halar® 1400LC are:
Typical application of Halar® 1400LC: Fabrics/Fibers |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 430 to 550 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.5 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 73 | ASTM D785 | |
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 1780 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C | 30.0 | MPa | |
| Break, 23°C | 19.0 to 29.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C | 1.0 to 10 | % | |
| Break, 23°C | 1.0 to 10 | % | |
| Flexural Modulus 4(23°C) | 1690 | MPa | ASTM D790 |
| Flexural Strength 5(23°C) | 45.0 to 47.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.20 | ||
| Taber Abrasion Resistance (1000 Cycles, 500 g, CS-17 Wheel) | 5.00 | mg |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.20 mm | 19 | J/m | |
| 23°C, 3.20 mm | 25 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 109 | °C | |
| 1.8 MPa, Unannealed | 68.0 | °C | |
| Brittleness Temperature | 20.0 | °C | ASTM D746A |
| Glass Transition Temperature | 85.0 | °C | DMA |
| Melting Temperature | 242 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 222 | °C | ASTM D3418 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat (23°C) | 962 | J/kg/°C | ASTM D3418 |
| Thermal Conductivity (40°C) | 0.15 | W/m/K | ASTM C177 |
| Crystallization Heat | 40.0 | J/g | ASTM D3418 |
| Heat of Fusion | 42.0 | J/g | ASTM D3418 |
| Thermal Stability - 1% mass loss, N2 | 300 | °C | TGA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 6(23°C) | 5.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 3.20 mm) | 14 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 2.57 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 52 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 2.5 mm/min |
| 5 . | 2.5 mm/min |
| 6 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP501M | LyondellBasell Industries | PP Homopolymer | Moplen |
| WEVO-CHEMIE Polyurethanes PU 925/1M/600 | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| Xuchuan XCW-8260HT | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Badamid® B70 GF50 | Bada AG | Nylon 6 | Badamid® |
| Bergamid™ B70 red RAL3001 | PolyOne Corporation | Nylon 6 | Bergamid™ |