Grivory® HT3Z LF black 9564
| Category: | Nylon 10T/X , Polyamide 10T/X Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grivory® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KOpadO_Grivory-HT3Z-LF-black-9564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grivory® HT3Z LF black 9564 is a Polyamide 10T/X Copolymer (Nylon 10T/X) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grivory® HT3Z LF black 9564 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 1.8 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 140 | 140 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2700 | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | 90 | kJ/m² | |
| 23°C | 100 | 95 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 110 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 85.0 | -- | °C | ISO 75-2/C |
| Maximum Use Temperature | Internal Method | |||
| Long Term | 140 | -- | °C | |
| Short Term | 240 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA10T/X, MH,12-030 | -- | ISO 1874 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 8.0E-5 | -- | cm/cm/°C | |
| Transverse | 8.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 400 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Advanced Composites ADX-5028 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Haysite Plastics Heatmeiser® | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Hanwha Total PP BI300 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| POLYCOMPO PE SP2520 | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |
| neogol® A552 Z005 | API SpA | TPO (POE) | neogol® |