Generic PESU - Carbon Fiber
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nKmYHY_Generic-PESU---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PESU - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.38 - 1.51 | g/cm³ | ASTM D792 |
| 23°C | 1.42 - 1.69 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.092 - 0.20 | % | ASTM D955 |
| 23°C | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 - 0.42 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5860 - 9900 | MPa | ASTM D638 |
| Tensile Stress | |||
| Fracture, 23°C | 90.0 - 92.4 | MPa | ISO 527-2 |
| 23°C | 103 - 173 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 1.5 - 3.0 | % | ASTM D638 |
| Flexural Modulus | |||
| 23°C | 5170 - 23700 | MPa | ASTM D790 |
| 23°C | 6300 - 22900 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 165 - 303 | MPa | ASTM D790 |
| 23°C | 125 - 305 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 52 - 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 480 - 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 204 - 211 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 - 270 | °C | ISO 75-2/A |
| CLTE - Flow | |||
| -- | 1.3E-5 - 3.8E-5 | cm/cm/°C | ASTM D696 |
| -- | 4.0E-6 - 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.1E+2 - 1.2E+10 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+2 - 1.2E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 349 - 365 | °C | |
| Middle Temperature | 357 - 370 | °C | |
| Front Temperature | 357 - 377 | °C | |
| Processing (Melt) Temp | 350 - 362 | °C | |
| Mold Temperature | 148 - 161 | °C | |
| Injection Pressure | 86.2 - 121 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PESU - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® GS431 | Vyncolit N.V. | Phenolic | Vyncolit® |
| WPP TPO TPO-3985 P Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Nanjing Hongrui PA66 A353 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| ESTASAN SAN 2000 | Cossa Polimeri S.r.l. | SAN | ESTASAN |
| Braskem PP DC705.01 | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |