TAISOX 2210
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pOgIcg_TAISOX-2210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 2210 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molded film. The main features of TAISOX 2210 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 186 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 235 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 10.3 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 41.2 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 33.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 760 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 260 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 360 | g | ASTM D1922 |
| TD : 38 µm, blown film | 820 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 51 | ASTM D2457 | |
| Clarity | 65.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTALON™ E1600MU | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| EVALENE® PP PRJ1501 | JG Summit Petrochemical Corporation | PP Random Copolymer | EVALENE® PP |
| EGYPTENE HD 5211 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| Sylvin 9600-95 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ PX0844 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |