Visico™ LE4421/Ambicat™ LE4472 Datasheet,XLPE,Borealis AG-SHANGHAI SUSHENG

Visico™ LE4421/Ambicat™ LE4472

Category:	XLPE , Crosslinked Polyethylene
Manufacturer:	Borealis AG
Trademark:	Visico™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	nI7AF5_Visico-LE4421-Ambicat-LE4472.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Visico LE4421 / Ambicat LE4472 is a silane crosslinkable black compound designed for covering/insulation of overhead cables. The base material Visico LE4421 in combination with the catalyst masterbatch Ambicat LE4472 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water. When properly mixed, addition of 7 parts of Ambicat LE4472 to 93 parts of Visico LE4421 , insulation with excellent thermo-oxidative stability, also in contact with copper as will as aluminium, is achieved. The final product will contain nominal 2,25% of fine size carbon black ensuring excellent weatherability. Visico LE4421 / Ambicat LE4472 contains antioxidant, metal deactivator and a drying agent. Visico LE4421 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst. Visico LE4421 / Ambicat LE4472 in combination meets the applicable requirements as below when processed using extrusion practice and testing procedure: ANSI/ICEA S-70-547 ASTM D 1248 Type II, Class C, Category 4 HD 603 S1 HD 626 S1 (TIX-2, TIX-4, TIX-6, TIX-9) IEC 60502-1 NEMA WC 71 NEMA WC 70 The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information. The base material Visico LE4421 in combination with the catalyst masterbatch Ambicat LE4472 is a ready-made two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. Visico LE4421 is based upon a cost optimised low density polyethylene, copolymerised with vinyl silane. The catalyst/carbon black masterbatch, Ambicat LE4472 , contains a novel, patented, environmentally friendly crosslinking catalyst and is completely free from heavy metals.

Message

Visico LE4421 / Ambicat LE4472 is a silane crosslinkable black compound designed for covering/insulation of overhead cables.

The base material Visico LE4421 in combination with the catalyst masterbatch Ambicat LE4472 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water.

When properly mixed, addition of 7 parts of Ambicat LE4472 to 93 parts of Visico LE4421 , insulation with excellent thermo-oxidative stability, also in contact with copper as will as aluminium, is achieved. The final product will contain nominal 2,25% of fine size carbon black ensuring excellent weatherability.

Visico LE4421 / Ambicat LE4472 contains antioxidant, metal deactivator and a drying agent. Visico LE4421 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst.

Visico LE4421 / Ambicat LE4472 in combination meets the applicable requirements as below when processed using extrusion practice and testing procedure:

ANSI/ICEA S-70-547

ASTM D 1248 Type II, Class C, Category 4

HD 603 S1

HD 626 S1 (TIX-2, TIX-4, TIX-6, TIX-9)

IEC 60502-1

NEMA WC 71

NEMA WC 70

The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information.

The base material Visico LE4421 in combination with the catalyst masterbatch Ambicat LE4472 is a ready-made two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. Visico LE4421 is based upon a cost optimised low density polyethylene, copolymerised with vinyl silane. The catalyst/carbon black masterbatch, Ambicat LE4472 , contains a novel, patented, environmentally friendly crosslinking catalyst and is completely free from heavy metals.

General Information
Additive	Antioxidant Carbon Black (2%) Drying Agent Metal Deactivator Scorch Resistant
Features	Antioxidant Crosslinkable Fast Cure Good Processability Good Surface Finish Low Density Low Die Swell
Uses	Power Cable Jacketing Wire & Cable Applications
Agency Ratings	ANSI/ICEA S-70-547 ASTM D 1248, II, Class C, Cat. 4 HD 603 S1 IEC 60502-1 NEMA WC-70 , WC-71
Appearance	Black
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density ¹	0.933	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F20)	> 96.0	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 1 sec)	52		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	> 15.0	MPa	ISO 527-2/250
Tensile Strain (Break)	> 300	%	ISO 527-2/250

Aging	Nominal Value	Unit	Test Method
Retention of Tensile Properties - After Ageing 240 h (135°C)	> 25	%	IEC 60811-1-2

Thermal	Nominal Value	Unit	Test Method
Hot Set			IEC 60811-2-1
200°C ²	0.0	%
200°C ³	60	%

Additional Information	Nominal Value	Unit
Crosslinking
23°C, 700.0 µm ⁴	1.5	day
23°C, 1.80 mm ⁵	6.0	day
90°C, 700.0 µm ⁶	< 15.0	min
90°C, 1.80 mm ⁷	1.00	hr

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Electric Strength	> 20	kV/mm	IEC 60243-1
Dielectric Constant (50 Hz)	< 2.50		IEC 60250
Dissipation Factor (50 Hz)	< 6.0E-4		IEC 60250

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	150	°C
Cylinder Zone 2 Temp.	170	°C
Cylinder Zone 3 Temp.	170	°C
Cylinder Zone 4 Temp.	170	°C
Die Temperature	170	°C

Note Message
1 .	Mixture 93:7, ISO 1872-2
2 .	Permanent deformation, 0.20 MPa
3 .	Elongation under load, 0.20 MPa
4 .	In air, 50 % humidity
5 .	In air, 50 % humidity
6 .	Sauna or water bath
7 .	Sauna or water bath

Resin Grade	Manufacturer	Category	Trademark
MarFlex® 5563	Chevron Phillips Chemical Company LLC	LDPE	MarFlex®
RAMOFIN PPC371B50	Polyram Ram-On Industries	PP Copolymer	RAMOFIN
RheTech Polypropylene CC30P100-00	RheTech, Inc.	PP, Unspecified	RheTech Polypropylene
Sylvin 9077-94 Black 262	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Lionpol IM-40082	Lion Polymers Incorporated	TPE	Lionpol