DOWLEX™ 2062GC
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ToeZ7L_DOWLEX-2062GC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dowlex™ 2062GC Polyethylene Resin is an ethylene 1-octene copolymer, suitable for cast film applications as well as excellent carrier resin for highly filled compounds. It offers superior stiffness in combination with excellent puncture resistance and optical properties, making it to a resin perfectly designed to meet converters down gauging needs. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.939 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Resistance (20 µm) | 6.30 | J/cm³ | ASTM D5748 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 37.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 24.0 | MPa | ASTM D882 |
| MD : 20 µm 1 | 9.80 | MPa | ASTM D882 |
| TD : 20 µm 2 | 11.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 490 | % | ASTM D882 |
| TD : Break, 20 µm | 720 | % | ASTM D882 |
| Elmendorf Tear Strength 3 | ASTM D1922 | ||
| MD : 20 µm | 50 | g | ASTM D1922 |
| TD : 20 µm | 210 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm) | 84 | ASTM D2457 | |
| Haze (20.0 µm) | 2.7 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Cast film extrusion conditions: Melt Temperature: 220°C Die gap: 0.7 mm Film thickness: 20 microns |
| Note Message | |
|---|---|
| 1 . | @ 5% Elongation |
| 2 . | @ 5% Elongation |
| 3 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210M40 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| NORYL™ FE1630PW resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| Electrafil® PEI 04001 MB | Techmer Engineered Solutions | PEI | Electrafil® |
| Geon™ Vinyl Rigid Molding M7500 | PolyOne Corporation | PVC Alloy | Geon™ Vinyl Rigid Molding |
| Sylvin 5401-65 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |